摘要This study focuses on understanding the deicing salt corrosion mechanism affecting highway roadside concrete structures and identifying appropriate protective measures. Initially, the mechanism of salt corrosion on roadside concrete is elucidated through thorough research and investigation. Subsequently, the effectiveness of protective materials such as acrylic, polyurethane, and epoxy coatings in mitigating salt corrosion in concrete is assessed by simulating salt corrosion conditions on the concrete surface. Optimizing the material formula based on the tests more effectively mitigates the corrosion effect. Results indicate that salt corrosion primarily results from the permeation of salts into concrete, triggering physiochemical corrosion. It is observed that all three types of protective materials significantly decelerate concrete corrosion caused by salt, demonstrating effective anti-corrosion properties. Among these, the optimized formulation of polyurethane coating ’C’ demonstrates superior permeability and resistance to chemical corrosion. It effectively prevents the ingress of salt into the concrete, thereby reducing the occurrence of salt corrosion in concrete. The low cost of these measures indicates their suitability for widespread implementation.
Abstract：This study focuses on understanding the deicing salt corrosion mechanism affecting highway roadside concrete structures and identifying appropriate protective measures. Initially, the mechanism of salt corrosion on roadside concrete is elucidated through thorough research and investigation. Subsequently, the effectiveness of protective materials such as acrylic, polyurethane, and epoxy coatings in mitigating salt corrosion in concrete is assessed by simulating salt corrosion conditions on the concrete surface. Optimizing the material formula based on the tests more effectively mitigates the corrosion effect. Results indicate that salt corrosion primarily results from the permeation of salts into concrete, triggering physiochemical corrosion. It is observed that all three types of protective materials significantly decelerate concrete corrosion caused by salt, demonstrating effective anti-corrosion properties. Among these, the optimized formulation of polyurethane coating ’C’ demonstrates superior permeability and resistance to chemical corrosion. It effectively prevents the ingress of salt into the concrete, thereby reducing the occurrence of salt corrosion in concrete. The low cost of these measures indicates their suitability for widespread implementation.
XIANG Guo-qiang, TANG Xiong, ZOU Jie, ZHAO Li-dong. Study on Deicing Salt Corrosion Mechanism and Protective Materials of Highway Roadside Concrete Structures[J]. Journal of Highway and Transportation Research and Development, 2024, 18(1): 63-72.
XIANG Guo-qiang, TANG Xiong, ZOU Jie, ZHAO Li-dong. Study on Deicing Salt Corrosion Mechanism and Protective Materials of Highway Roadside Concrete Structures. Journal of Highway and Transportation Research and Development, 2024, 18(1): 63-72.
[1] ZHANG Yun-qing, YU Hong-fa, WANG Jia-chun. Influence of Bubble Structure Characteristics on Salt Frost Resistance of Concrete[J]. Journal of South China University of Technology, 2010, 38(11):7-11.(in Chinese) [2] LI Lei. Research on Sulfate And Magnesium Salt Double Erosion Resistance of High Sulfate Resistant Cement Concrete[D]. Urumqi:Xinjiang Agricultural University, 2016.(in Chinese) [3] ZHANG Ai-lian, ZHANG Lin-chun, DENG Hong-wei. Study on Salt Frost Resistance of Fly Ash Ceramsite Concrete[J]. Concrete, 2010(4):59-61.(in Chinese) [4] WANG Qian-li, YAO Yan, WANG Ling, et al. Permeability of Steel Slag Slag Concrete Under Salt Freezing[J]. Industrial building, 2013(2):113-117.(in Chinese) [5] SHEN Hua-rong, LU Xiao-lin, GAO Pei-wei, et al. Relationship Between the Air Void System and Frost-Salt Resistance of Concrete[J]. Concrete, 2012(8):8-9, 13.(in Chinese) [6] LIU Y. Quality Control and Technical Countermeasures of Anticorrosive Concrete in Coastal Areas[J]. Transportation World, 2020(Z2):116-117.(in Chinese) [7] FAN Jun-feng, JIN Zu-quan, JIANG Yu-dan. Study on Shrinkage and Sulfate Corrosion of Anticorrosive Concrete[J]. Journal of Qingdao University of Technology, 2018, 39(2):24-28.(in Chinese) [8] GAO H. Study on Effect of Mineral Admixtures on Corrosion Resistance of Concrete[D]. Wuhan:Wuhan University, 2017.(in Chinese) [9] HU Zheng-tao, LI Guan-guo, YANG Hai-cheng, et al. Durability Design of Concrete Structure of Tongminghai Large Bridge in South China[J]. Corrosion and Protection, 2023, 44(2):87-93.(in Chinese) [10] WANG Kang-chen, FANG Xiang, FAN Zhi-hong, et al. Durability Design of Concrete Structure in Deep Tunnel[J]. Corrosion and Protection, 2022, 43(12):88-94, 99.(in Chinese) [11] TANG Shi-run, LIN Peng-zhen, ZHAO Fu-kang. Fatigue Stress Analysis of Surface Coatings on Steel-Concrete Composite Beams Under Live Load Effect[J]. Corrosion and Protection, 2021, 42(9):66-73, 94.(in Chinese) [12] CAI Sen, PEI Guo-qiang, ZHANG Yong. Outside the Concrete Lining in the Application of Anticorrosive Design and Construction of Steel Tubular Piles[J]. Port&Waterway Engineering, 2015(1):204-208.(in Chinese) [13] WANG Tao, DU Cun-shan, ZHU He-quan, et al. Research on Corrosion Prevention Technology of Co-permeating Passivated Sealing Composite for Attached Steel Structure of Concrete Bridge[J]. Materials Protection, 2021, 54(10):73-77, 116.(in Chinese) [14] TANG Shi, ZHANG Peng-fei, ZHANG Jin-hao, et al. Research on the Development and Properties of Concrete Appearance Beautifying Materials[J]. Materials Protection, 2021, 54(7):122-127.(in Chinese) [15] ZHANG Hui-li, LIU Ze, ZHANG Wei-dong. Regression Analysis of Concrete Coating Service Life Based on Cox Survival Model[J]. Materials Protection, 2021, 54(5):24-28.(in Chinese)
2024, Vol. 18 