A Study of the Fretting Wear of Parallel Wire Bundle Stay Cable
王天鹏1,2, 周欣颖1, 陈溢广1
1. School of Civil Engineering, Central South University of Forestry and Technology, Changsha Hunan 410004, China; 2. School of Civil Engineering, Changsha University of Science & Technology, Changsha Hunan 410114, China
A Study of the Fretting Wear of Parallel Wire Bundle Stay Cable
WANG Tian-peng1,2, ZHOU Xin-ying1, CHEN Yi-guang1
1. School of Civil Engineering, Central South University of Forestry and Technology, Changsha Hunan 410004, China; 2. School of Civil Engineering, Changsha University of Science & Technology, Changsha Hunan 410114, China
摘要In order to accurately evaluate the durability stay cables of parallel steel wire bundle for bridges, the study is conducted on fretting wear during service. First, based on the structure of the parallel steel wire rope, the squeezing forces between the steel wires at different positions caused by the twisting angle and the sheath clamping effect are calculated separately. Then, a contact mechanics model between parallel steel wires is established, and a calculation method for the depth of fretting wear of parallel steel wires is proposed based on the amplitude and frequency of fretting. Finally, the wear depth of parallel steel wire cables in a cable-stayed bridge that has been in service for 20 a is calculated and compared with the measured results.The result shows that (1) the contact mechanics model can accurately calculate the wear depth of wires at different positions of parallel wire rope during service; (2) in the length direction of the cable, the wear degree of the steel wire near the end is greater than that of the middle steel wire, from the section distribution of the cable, the wear degree of the outer steel wire is light, the wear of the steel wire near the center of the circle is serious, and the theoretical calculation results are basically consistent with the detection results of the old cable of the real bridge; (3)the development of steel wire wear depth shows a power function rule of first fast and then slow with the increase of time, the wear rate increases with the increase of contact force between steel wires, vibration frequency and amplitude of cable; (4)the zinc coating of steel wire in the example will be worn out in 4.5 a to 9 a, which is far lower than the failure time of zinc coating caused by environmental corrosion. Fretting wear will lead to premature failure of zinc coating and shorten the initiation time of fatigue crack. If fretting wear between parallel steel wires is not considered, the life evaluation of cable will be unsafe.
Abstract：In order to accurately evaluate the durability stay cables of parallel steel wire bundle for bridges, the study is conducted on fretting wear during service. First, based on the structure of the parallel steel wire rope, the squeezing forces between the steel wires at different positions caused by the twisting angle and the sheath clamping effect are calculated separately. Then, a contact mechanics model between parallel steel wires is established, and a calculation method for the depth of fretting wear of parallel steel wires is proposed based on the amplitude and frequency of fretting. Finally, the wear depth of parallel steel wire cables in a cable-stayed bridge that has been in service for 20 a is calculated and compared with the measured results.The result shows that (1) the contact mechanics model can accurately calculate the wear depth of wires at different positions of parallel wire rope during service; (2) in the length direction of the cable, the wear degree of the steel wire near the end is greater than that of the middle steel wire, from the section distribution of the cable, the wear degree of the outer steel wire is light, the wear of the steel wire near the center of the circle is serious, and the theoretical calculation results are basically consistent with the detection results of the old cable of the real bridge; (3)the development of steel wire wear depth shows a power function rule of first fast and then slow with the increase of time, the wear rate increases with the increase of contact force between steel wires, vibration frequency and amplitude of cable; (4)the zinc coating of steel wire in the example will be worn out in 4.5 a to 9 a, which is far lower than the failure time of zinc coating caused by environmental corrosion. Fretting wear will lead to premature failure of zinc coating and shorten the initiation time of fatigue crack. If fretting wear between parallel steel wires is not considered, the life evaluation of cable will be unsafe.
基金资助:Supported by the National Basic Research Development Program of China (973 Program) (No. 2015CB057705); National Natural Science Foundation of China (No. 51778068); Science and Technology Project of Department of Communications of Hunan Province (No. 201527)
通讯作者:
WANG Tian-peng
引用本文:
王天鹏, 周欣颖, 陈溢广. A Study of the Fretting Wear of Parallel Wire Bundle Stay Cable[J]. Journal of Highway and Transportation Research and Development, 2023, 17(4): 7-16.
WANG Tian-peng, ZHOU Xin-ying, CHEN Yi-guang. A Study of the Fretting Wear of Parallel Wire Bundle Stay Cable. Journal of Highway and Transportation Research and Development, 2023, 17(4): 7-16.
[1] BHATTI N A, WAHAB M A. Fretting Fatigue Crack Nucleation:A Review[J]. Tribology International, 2018, 121:121-138. [2] LIU Z, GUO T, HAN D, et al. Experimental Study on Corrosion-fretting Fatigue Behavior of Bridge Cable Wires[J]. Journal of Bridge Engineering, 2020, 25(12):1-9. [3] ZHANG De-kun, GE Shi-rong. Research on the Evaluation Parameters and Theory Model of Fretting Wear between Steel Wires[J]. Tribology, 2005, 25(4):50- 54. (in Chinese) [4] ZHANG De-kun, GE Shi-rong. Research on the Contact Mechanisms in the Process of Fretting Wear between Steel Wires[J]. Journal of Mechanical Strength, 2007, 29(01):148-151. (in Chinese) [5] WANG D G, ZHANG D K, WANG S Q, et al. Finite Element Analysis of Hoisting Rope and Fretting Wear Evolution and Fatigue Life Estimation of Steel Wires[J]. Engineering Failure Analysis, 2013, 27:173-193. [6] WANG D G, LI X W, WANG X R, et al. Dynamic Wear Evolution and Crack Propagation Behaviors of Steel Wires during Fretting-fatigue[J]. Tribology International, 2016, 101:348-355. [7] PÉRIER V, DIENG L, GAILLET L, et al. Fretting-fatigue Behaviour of Bridge Engineering Cables in a Solution of Sodium Chloride[J]. Wear, 2009, 267(1-4):308-314. [8] PÉRIER V, DIENG L, GAILLET L, et al. Influence of an Aqueous Environment on the Fretting Behaviour of Steel Wires Used in Civil Engineering Cables[J]. Wear, 2011, 271(9-10):1585-1593. [9] GUO T, LIU Z, CORREIA J, et al. Experimental Study on Fretting-fatigue of Bridge Cable Wires[J]. International Journal of Fatigue, 2020, 131, 105321:1-10. [10] LIU Mu-yu, CHEN Qi-feng, WU Zhi-qiang. Time-dependent Reliability Analysis of Strand Cables of Cablestayed Bridges Considering Fretting-fatigue Factor[J]. China Civil Engineering Journal, 2012, 45(7):141-147. (in Chinese) [11] GAO Wen-bo, YUAN Yang-guang, HUANG Ping-ming, et al. Safety Assessment of Steel Strand Stay Cable Under Customized Transport Vehicle Load Considering Strength Degradation[J]. China Journal of Highway and Transport, 2020, 33(8):169-181. (in Chinese) [12] YANG Mo-xin. Simulation Analysis of Friction Damage to the Parallel Wire[D]. Changsha:Changsha University of Science & Technology, 2018:31-42. (in Chinese) [13] ZHENG Gang, WANG Peng, TANG Guang-wu. Natural Environment Corrosion of Chinese Materials[M]. Beijing:China Communications Press Co., Ltd, 2015:105-155. (in Chinese) [14] GB/T 18365-2018, Hot-extruded PE Protection Paralleled High Strength Wire Cable for Cable-stayed Bridge[S]. (in Chinese) [15] WANG Xiu-yong, CHEN Zheng-qing. Wind-rain Induced Vibration and its Control on Stay Cables of Cable-Stayed Bridges[J]. China Civil Engineering Journal, 2003, 36(6):53-59. (in Chinese) [16] GAO Xin. Analysis Methods for Suspender Damage and System Reliability of Existing Concrete Filled Steel Tubular Arch Bridge[D]. Harbin:Harbin Institute of Technology, 2011:87-90. [17] XU Hong. Mechanical Analysis and Safety Evaluation of Bridge Damaged Cable[D]. Xi'an:Chang'an University, 2008:124-126. [18] CAO Chu-nan. Natural Environment Corrosion of Chinese Materials[M]. Beijing:Chemical Industry Press, 2004:92-98. (in Chinese)
2023, Vol. 17 